H12 H14 H16 H18 Temper 1145 Aluminium Alloy With Strong Electric Properties
Product introduction of 1145 Aluminum Sheet:
Aluminium / Aluminum 1145 alloy is a difficult alloy to machine. It is slightly easier to machine in the H16, 18 or 19 tempers than in the softer or annealed temper form.
Property Specification of 1145 Aluminum Sheet:
| Thermal Properties | Metric | English | Comments |
| Heat of Fusion | 390 J/g | 168 BTU/lb | / |
 CTE, linear | 21.8 µm/m-°C | 12.1 µin/in-°F | / |
| Temperature -50.0 - 20.0 °C | Temperature -58.0 - 68.0 °F |
| | 23.6 µm/m-°C | 13.1 µin/in-°F | / |
| Temperature 20.0 - 100 °C | Temperature 68.0 - 212 °F |
| | 24.5 µm/m-°C | 13.6 µin/in-°F | / |
| Temperature 20.0 - 200 °C | Temperature 68.0 - 392 °F |
| | 25.5 µm/m-°C | 14.2 µin/in-°F | / |
| Temperature 20.0 - 300 °C | Temperature 68.0 - 572 °F |
| Specific Heat Capacity | 0.904 J/g-°C | 0.216 BTU/lb-°F | / |
| Thermal Conductivity | 230 W/m-K | 1600 BTU-in/hr-ft²-°F | / |
| Melting Point | 646 - 657 °C | 1190 - 1210 °F | / |
| Solidus | 646 °C | 1190 °F | / |
| Liquidus | 657 °C | 1210 °F | / |
| Optical Properties | Metric | English | Comments |
| Emissivity (0-1) | 0.04 | 0.04 | At 9.3 micron wavelength |
| Reflection Coefficient, Visible (0-1) | 0.96 | 0.96 | 0.3-10 micron wavelength |
| Processing Properties | Metric | English | Comments |
| Annealing Temperature | 343 °C | 650 °F | |
| |
| Component Elements Properties | Metric | English | Comments |
| Aluminum, Al | >= 99.45 % | >= 99.45 % | Specified |
| Copper, Cu | <= 0.05 % | <= 0.05 % | / |
| Magnesium, M | <= 0.05 % | <= 0.05 % | / |
| Manganese, Mn | <= 0.05 % | <= 0.05 % | / |
| Other, each | <= 0.03 % | <= 0.03 % | / |
| Si+Fe | <= 0.55 % | <= 0.55 % | / |
| Titanium, Ti | <= 0.03 % | <= 0.03 % | / |
| Vanadium, V | <= 0.05 % | <= 0.05 % | / |
| Zinc, Zn | <= 0.05 % | <= 0.05 % | / |
Heat Treatment of 1145 Aluminum Alloy:
Aluminium / Aluminum 1145 alloy is a non-heat treatable alloy that can be hardened by cold working.
Cold Working of 1145 Aluminum Alloy:
Aluminium / Aluminum 1145 alloy is extremely easy to cold work in the softer tempers such as annealed, H12, 14, 16 tempers. It is a lot more difficult with harder tempers but it is still possible.
Annealing of 1145 Aluminum Alloy:
Annealing can be performed at 343°C (650°F) for a suitable amount of time and then air cooled.
Hardening of 1145 Aluminum Alloy:
Aluminium / Aluminum 1145 alloy can be hardened by cold working only.
Packaging And Product Details of 1145 Aluminum Alloy:
Product Tags:
|
|
H12 H14 H16 H18 Temper 1000 Aluminum Sheet With Strong Electric Properties Images
|